  • LT series thermal conductive ceramics
  • 主图1.jpg

LT series thermal conductive ceramics

Category:Thermal conductive ceramic hea

Introduction:

National Advisory Service Hotline:86-0755-29082440

PurchaseAdvisory

  • Details
  • Parameter


LT240 thermal conductive ceramic has a high thermal conductivity : 24w/m。k, it is of simple construction and small volume, but it can
resist acid and alkali corrosio, work in high temperature and pressure and of stable performance for a long time.0.635mm, 1.0mm, 2.0mm,
3.0mm, 4.0mm can be offered for TO-220, TO-247, TO-264, TO-3P sizes,customized size is available, ROHS is compliant.

Typical applications:
IC, MOS, transistor, schottky, IGBT, high density switch
power supply, HF communications equipment and
brazing machine。

Physical properties:

Test Item

单位Unit

96% Aluminum oxide

 Density

G/CM³

3.90

 Water absorption

%

0

 Thermal expansion coefficient

10-6/K

8.5

 Young's modulus

GPa

340

 Poisson ratio

/

0.22

 Hardness  (Hv)

MPa

1650

Bending strength  (room temperature)

MPa

310

 

Bending strength  (700°C)

MPa

230

Compression strength  (room temperature)

MPa

2200

 Fracture toughness

MPa'm½

4.2

Thermal conductivity  (room temperature)

W/m.k

24

 Insulation strength

KV/mm

10

Long-term working temperature

1480

 Ratio resistivity

Ω•mm²/m

1016

Maximum service temperature  (no-load)

°C

1750

Acid-base and corrosion resistance

/

 Strong

 Refractoriness

°C

2000

Test Item

单位Unit

96% Aluminum oxide

 Density

G/CM³

3.90

 Water absorption

%

0

 Thermal expansion coefficient

10-6/K

8.5

 Young's modulus

GPa

340

 Poisson ratio

/

0.22

 Hardness  (Hv)

MPa

1650

Bending strength  (room temperature)

MPa

310

 

Bending strength  (700°C)

MPa

230

Compression strength  (room temperature)

MPa

2200

 Fracture toughness

MPa'm½

4。2

Thermal conductivity  (room temperature)

W/m.k

24

 Insulation strength

KV/mm

10

Long-term working temperature

1480

 Ratio resistivity

Ω•mm²/m

1016

Maximum service temperature  (no-load)

°C

1750

Acid-base and corrosion resistance

/

 Strong

 Refractoriness

°C

2000