  • Aluminum Nitride Conductive Ceramic Film

Aluminum Nitride Conductive Ceramic Film

Category:Thermal conductive ceramic hea

Introduction:

National Advisory Service Hotline:86-0755-29082440

PurchaseAdvisory

  • Details
  • Parameter



Conductivity 180W/m.k One of the highest thermal conductivity materials

in metallic materials (7-10 times of alumina ceramic).

吉林快3开奖 Excellent mechanical properties, good processing, high precision, smooth

surface, no microcracks, Bending, etc.Low dielectric constant and dielectric

loss, reliable electrical insulation performance。Non-toxic,High temperature

of 1800 degrees, oil resistant, chemical resistant, and similar to the thermal expansion coefficient of silicon,Without hygroscopic property, stable performance and high reliability in high temperature and high humidity.Along with the micro electric.The extensive development of the microelectronic equipment, the high thermal conductivity nitride ceramic film is widely valued and applied.

 Product Feature

●Extremely high thermal conductivity

●High temperature and high humidity 

●Good insulation 

●Good chemical stability


Typical applications

●Application of optical communication devices  ●LED industry 

●High frequency microwave application           ●Power electronic components 

●Large efficiency power supply module           ●Special refrigerator

●The thermal module substrate                     ●Car electronic

Physical Properties

Property Sort

Property Content

Unit

Test Result

 

 

Basic Properties

Appearance/Color

 

Dense, Fine Crystal/Off White

Water Absorption

%

0

Dimensional Tolerance

mm

≤±0.1

Thickness Tolerance

mm

≤±0。05

Volume Density

g/cm³

3.3

Surface Roughness Ra

μm

0。25~0。5

Warpage

length‰

≤2‰

 

Mechanical Properties

Flexural Strength

MPa

≥450

Modulus Of Elasticity

GPa

320

Moh’s Hardness

 

8

 

Electrical Properties

Volume Resistance

Ω。cm

≥1013

Dielectric Constant

1M Hz

8.7

Dielectric Loss

1M Hz

3×10-4

Dielectric Strength

KV/mm

≥17

 

Thermal Properties

Thermal Expansivity

X106/

4.4

Specific Heat

J/kg。k

738

Thermal Conductivity (30)

W/m.k

≥180

Regular Size:

     Thickness(mm

Sizemm

0。385

0.5

0.635

0.75

1.0

Length*Width

50。8*50。8/76*76/101。6*101。6/114。3*114。3/127*127/140*190mm

Customized size and shape is available.

Property Sort

Property Content

Unit

Test Result

 

 

Basic Properties

Appearance/Color

 

Dense, Fine Crystal/Off White

Water Absorption

%

0

Dimensional Tolerance

mm

≤±0.1

Thickness Tolerance

mm

≤±0。05

Volume Density

g/cm³

3.3

Surface Roughness Ra

μm

0.25~0.5

Warpage

length‰

≤2‰

 

Mechanical Properties

Flexural Strength

MPa

≥450

Modulus Of Elasticity

GPa

320

Moh’s Hardness

 

8

 

Electrical Properties

Volume Resistance

Ω.cm

≥1013

Dielectric Constant

1M Hz

8.7

Dielectric Loss

1M Hz

3×10-4

Dielectric Strength

KV/mm

≥17

 

Thermal Properties

Thermal Expansivity

X106/

4。4

Specific Heat

J/kg.k

738

Thermal Conductivity (30)

W/m.k

≥180

Regular Size:

     Thickness(mm

Sizemm

0.385

0.5

0.635

0。75

1.0

Length*Width

50.8*50.8/76*76/101.6*101.6/114.3*114.3/127*127/140*190mm

Customized size and shape is available.